|Title:||Growth of LiCoO2 single crystals by the TSFZ method|
|Publisher:||American Chemical Society|
|Citation:||Nakamura, S., Maljuk, A., Maruyama, Y., Nagao, M., Watauchi, S., Hayashi, T., Anzai, Y., Furukawa, Y., Ling, C. D., Deng, G., Avdeev, M., Büchner, B., & Tanaka, I. (2019). Growth of LiCoO2 single crystals by the TSFZ method. Crystal Growth & Design, 19(1), 415–420. doi:10.1021/acs.cgd.8b01503|
|Abstract:||We have grown LiCoO2 single crystals by the traveling solvent floating zone (TSFZ) growth with Li-rich solvent, having observed the incongruent melting behavior of LiCoO2 between 1100 and 1300 °C. The optimum growth conditions in terms of atmosphere and solvent composition were determined to be Ar flow and an atomic ratio Li/Co 85:15, respectively. The crystals grown using a conventional-mirror-type furnace contained periodic inclusions of a Co–O phase due to the influence of Co–O phase segregation on the stability of the molten zone during growth. By using a tilted-mirror FZ furnace, inclusion-free LiCoO2 crystals of about 5 mm in diameter and 70 mm long were obtained at a tilting angle θ = 10°. The grown crystals were confirmed to be single-domain by neutron Laue diffraction. © 2018 American Chemical Society|
|Appears in Collections:||Journal Articles|
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.