Microstructural and compositional analysis of strontium-doped lead zirconate titanate thin films on gold-coated silicon substrates
No Thumbnail Available
Date
2009-02
Journal Title
Journal ISSN
Volume Title
Publisher
Cambridge University Press
Abstract
This article discusses the results of transmission electron microscopy (TEM)-based characterization of strontium-doped lead zirconate titanate (PSZT) thin films. The thin films were deposited by radio frequency magnetron sputtering at 300°C on gold-coated silicon substrates, which used a 15 nm titanium adhesion layer between the 150 nm thick gold film and (100) silicon. The TEM analysis was carried out using a combination of high-resolution imaging, energy filtered imaging, energy dispersive X-ray (EDX) analysis, and hollow cone illumination. At the interface between the PSZT films and gold, an amorphous silicon-rich layer (about 4 nm thick) was observed, with the film composition remaining uniform otherwise. The films were found to be polycrystalline with a columnar structure perpendicular to the substrate. Interdiffusion between the bottom metal layers and silicon was observed and was confirmed using secondary ion mass spectrometry. This occurs due to the temperature of deposition (300°C) being close to the eutectic point of gold and silicon (363°C). The diffused regions in silicon were composed primarily of gold (analyzed by EDX) and were bounded by (111) silicon planes, highlighted by the triangular diffused regions observed in the two-dimensional TEM image. © 2009, Cambridge University Press
Description
Keywords
Silicon, Strontium, Transmission electron microscopy, PZT, Thin films, Mass spectroscopy
Citation
Sriram, S., Bhaskaran, M., Mitchell, D. R. G., Short, K. T., Holland, A. S., & Mitchell, A. (2009). Microstructural and compositional analysis of strontium-doped lead zirconate titanate thin films on gold-coated silicon substrates. Microscopy and Microanalysis, 15(1), 30-35. doi:10.1017/S1431927609090072