Hydrothermal synthesis, crystal structure, and superconductivity of a double-perovskite Bi oxide

Double-perovskite Bi oxides are a new series of superconducting materials, and their crystal structure and superconducting properties are under investigation. In this paper, we describe the synthesis and characterization of a new double-perovskite material that has an increased superconductive transition temperature of 31.5 K. The structure of the material was examined using powder neutron diffraction (ND), synchrotron X-ray diffraction (SXRD), and transmission electron microscopy (TEM). Rietveld refinement of the sample based on ND and SXRD data confirmed an A-site-ordered (K1.00)(Ba1.00)3(Bi0.89Na0.11)4O12 double-perovskite-type structure with the space group Im3̅m (No. 229). This structural analysis revealed the incorporation of Na with Bi in the structure and a bent bond between (Na, Bi)–O–(Na, Bi). TEM analyses also confirmed a cubic double-perovskite structure. This hydrothermally synthesized compound exhibited a large shielding volume fraction, exceeding 100%, with onset of superconductivity at ∼31.5 K. Its electrical resistivity dropped near onset at ∼28 K, and zero resistivity was confirmed below 13 K. The calculated band structure revealed that the metallicity of the compound and the flatness of the conduction bands near the Fermi level (EF) are important for the appearance of superconductivity. © 2015 American Chemical Society

Keywords

Perovskite, Bismuth oxides, Superconductors, Transition temperature, Neutron diffraction, X-ray diffraction, Transmission electron microscopy, Crystal structure

Citation

Rubel, M. H. K., Takei, T., Kumada, N., Ali, M. M., Miura, A., Tadanaga, K., Oka, K., Azuma, M., Yashima, M., Fujii, K., Magome, E., Moriyoshi, C., Kuroiwa, Y., Hester, J. R., & Avdeev, M. (2015). Hydrothermal synthesis, crystal structure, and superconductivity of a double-perovskite Bi oxide. Chemistry of Materials, 28(2), 459–465. doi:10.1021/acs.chemmater.5b02386