The variation with temperature and porosity, of the moduli rupture and elasticity of standard isostatically pressed and sintered beryllia

Simple item page
dc.contributor.authorVeevers, Ken_AU
dc.contributor.authorRotsey, WBen_AU
dc.date.accessioned2007-11-22T04:32:56Zen_AU
dc.date.accessioned2010-04-30T04:41:03Zen_AU
dc.date.available2007-11-22T04:32:56Zen_AU
dc.date.available2010-04-30T04:41:03Zen_AU
dc.date.issued1965-04en_AU
dc.description.abstractSome properties of isostatically pressed and sintered UOX beryllia, fabricated at Lucas Heights to a grain size of ≤3μ were measured. The modulus of rupture of material of density 2.86 to 2.90 g cm-3 was measured in four-point bending over the temperature range 20ºC to 1000ºC. The data could be represented by the equation: σf = 33,000 - 7.46T p.s.i. The total variance was 19.5 x 10 6 p.s.i. made up of a "within" batch variance, of 15.8 x 10 6 p.s.i. and a "between" batch variance of 3.7 x 10 6 p.s.i. The modulus of rupture at 20ºC was measured on material with a total porosity range of 4 to 35 per cent; the data could be represented by the equation: σ = σ0 exp(-2.44P) p.s.i. The modulus of elasticity was measured in four-point bending on 97-5 per cent, dense material and the data could be represented by the equation: E = (51.45 x 10 6)+(l.264x10 2 T)-(1.442+10-1T2)-(2.595x10-3T3) p.s.i. The modulus of elasticity was measured as a function of porosity in the range 2 to 36.4 per cent. The data could be represented by the equations E = Eo (1-1.47P) x 10 6 p.s.i.en_AU
dc.identifier.citationVeevers, K., & Rotsey, W. B. (1965). The variation with temperature and porosity, of the moduli rupture and elasticity of standard isostatically pressed and sintered beryllia. (AAEC/TM 290). Lucas Heights, NSW: Australian Atomic Energy Commission.en_AU
dc.identifier.govdoc838en_AU
dc.identifier.otherAAEC-TM-290en_AU
dc.identifier.placeofpublicationLucas Heights, New South Walesen_AU
dc.identifier.urihttp://apo.ansto.gov.au/dspace/handle/10238/828en_AU
dc.language.isoen_auen_AU
dc.publisherAustralian Atomic Energy Commissionen_AU
dc.subjectBeryllium oxidesen_AU
dc.subjectSintered materialsen_AU
dc.subjectSinteringen_AU
dc.subjectPorosityen_AU
dc.subjectElasticityen_AU
dc.subjectRupturesen_AU
dc.subjectTemperature rangeen_AU
dc.subjectPressingen_AU
dc.subjectCold pressingen_AU
dc.titleThe variation with temperature and porosity, of the moduli rupture and elasticity of standard isostatically pressed and sintered berylliaen_AU
Files
Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
AAEC-TM-290.pdf
Size:
660.73 KB
Format:
Adobe Portable Document Format
Description:
Download
Collections
Scientific and Technical Reports