Studies of the antiferrodistortive transition in EuTiO3

Abstract

Structural studies of EuTiO3, conducted using synchrotron x-ray powder diffraction, reveal the sensitivity of this material to defects. The presence of a single tetragonal–cubic (I4/mcm–Pm-3m) transition is confirmed. Neutron diffraction measurements show EuTiO3 to have a G-type antiferromagnetic arrangement. Examinations of the symmetry-adapted tetragonal strains demonstrate that the stoichiometry impacts on the continuous nature of this. The impact of defects on the electrical conductivity and magnetodielectric effect is also described. © 2014 IOP Publishing Ltd