|Title: ||Effects of Cu substitution on structural and magnetic properties of La0.7Pr0.3Fe11.4Si1.6 compounds|
|Authors: ||Md Din, MF|
|Issue Date: ||1-May-2013|
|Publisher: ||Elsevier Ltd.|
|Citation: ||Md Din, M. F., Wang, J. L., Zeng, R., Shamba, P., Debnath, J. C., & Dou, S. X. (2013). Effects of Cu substitution on structural and magnetic properties of La0.7Pr0.3Fe11.4Si1.6 compounds. Intermetallics, 36, 1-7.|
|Abstract: ||The structure and magnetic properties of the La0.7Pr0.3Fe11.4−xCuxSi1.6 compounds have been investigated by X-ray diffraction, scanning electron microscopy and magnetisation measurements. Cu substitution for Fe in La0.7Pr0.3Fe11.4−xCuxSi1.6 (x = 0, 0.06, 0.12, 0.23, 0.34) leads to a reduction in hysteresis loss, a decrease in magnetic entropy change but an increase in Curie temperature (TC). The influences of annealing processes at different temperatures on TC, magnetic hysteresis, and the magnetocaloric effect (MCE) of La0.7Pr0.3Fe11.4Si1.6 are investigated in detail. It has been found that a short-time and high temperature annealing process has benefits for the formation of the NaZn13 types as phase compared to a long-time and low temperature annealing process. © 2013, Elsevier Ltd.|
|Appears in Collections:||Journal Articles|
Files in This Item:
There are no files associated with this item.
Items in APO are protected by copyright, with all rights reserved, unless otherwise indicated.