    Characterisation of metakaolin-based geopolymers using beam-based and conventional PALS
    (Institute of Physics, 2010-08-01) Guagliardo, P; Roberts, J; Vance, ER; Weed, R; Sergeant, AD; Howie, A; Wilkie, P; Went, M; Sullivan, J; Williams, J; Samarin, S; Buckman, SJ
    The nano-porosity of metakaolin-based geopolymers and the effect of heat-treatment on porosity have been studied with conventional and beam-based positron annihilation lifetime spectroscopy (PALS). Conventional PALS found significant nano-porosity in the geopolymers, as indicated by the presence in the PALS spectrum of two long lifetime components, τ3 = 1.58 ns and τ4 = 47 ns, associated with pore diameters of approximately 0.5 and 3 nm respectively. The lifetime of the shorter component was found to decrease monotonically with successive heat treatments of 300°C and 600°C. Beam-based PALS, conducted at 5 keV, also indicated two long lifetime components, τ3 = 4.84 ns and τ4 = 54.6 ns. These are significantly longer than those observed by conventional PALS and the monotonic decrease of τ3 with successive heat treatments was not observed. As the beam-based PALS probed only the near-surface region, with an average implantation depth of about 350 nm, these results suggest that the near-surface structure may vary significantly from that of the bulk. This could be an inherent property of the samples or an artefact caused by surface effects or sample outgassing. © Copyright 2020 IOP Publishing
  • No Thumbnail Available
    Item
    Positron annihilation lifetime study of radiation-damaged natural zircons
    (Elsevier B.V., 2016-04-01) Roberts, J; Gaugliardo, PR; Farnan, I; Zhang, M; Vance, ER; Davis, J; Karatchevtseva, I; Knott, RB; Mudie, ST; Buckman, J; Sullivan, JP
    Zircons are a well-known candidate waste form for actinides and their radiation damage behaviour has been widely studied by a range of techniques. In this study, well-characterised natural single crystal zircons have been studied using Positron Annihilation Lifetime Spectroscopy (PALS). In some, but not all, of the crystals that had incurred at least half of the alpha-event damage of ∼1019 α/g required to render them structurally amorphous, PALS spectra displayed long lifetimes corresponding to voids of ∼0.5 nm in diameter. The long lifetimes corresponded to expectations from published Small-Angle X-ray Scattering data on similar samples. However, the non-observation by PALS of such voids in some of the heavily damaged samples may reflect large size variations among the voids such that no singular size can be distinguished or. Characterisation of a range of samples was also performed using scanning electron microscopy, optical absorption spectroscopy, Raman scattering and X-ray scattering/diffraction, with the degree of alpha damage being inferred mainly from the Raman technique and X-ray diffraction. The observed void diameters and intensities of the long lifetime components were changed somewhat by annealing at 700 °C; annealing at 1200 °C removed the voids entirely. The voids themselves may derive from He gas bubbles or voids created by the inclusion of small quantities of organic and hydrous matter, notwithstanding the observation that no voidage was evidenced by PALS in two samples containing hydrous and organic matter. © 2016 Elsevier B.V.