    Characterization of thermally stable diamond composite material
    (Scientific.Net, 2014-02-01) Luzin, V; Boland, JN; Avdeev, M; Li, XS
    Diamond composite materials are being used increasingly in cutting tools for both the mining and manufacturing industries. Except for the low pressure CVD and SPS methods, most SiC based diamond composites are produced under high pressure and high temperature (HPHT). The dominant binder phase is SiC and these composites are classed as thermally stable and are referred to as TSDC (thermally stable diamond composite). TSDC composites are produced by reactive sintering either within the diamond stability field, ~1500°C and ~5.5 GPa, or in the graphite phase field at ~1550°C and ~2 - 3.5 GPa as originally patented by Ringwood. Unlike the traditional polycrystalline diamond composite (PCD) that use Co as the binder phase and operate under restricted temperature conditions, usually less the 800°C, TSDC is Co-free allowing the operational temperature range for TSDC to be extended substantially. Extensive experimental research has been conducted at the CSIRO (Commonwealth Scientific & Industrial Research Organization) Rock Cutting Laboratory to assess the quality of TSDC products through a series of in-house tests that have been developed (abrasive wear test, compressive and shear testing) to facilitate their use in the mining industry. The focus is to prevent TSDC from premature failures in drilling and cutting operations. Since the wear resistance and performance in general, of TSDC cutting elements are strongly dependent on the phase composition, phase distribution (microstructures) and phase interaction (microstresses), detailed studies of TSDC have been undertaken using optical, SEM (with EDS and CL), Raman microscopy and radiographic imaging of macro defects as well as x-ray and neutron diffraction. Residual stress measurements were made using the neutron diffractometer Kowari at OPAL research reactor in the diamond and SiC phases in two TSDC samples. The microstresses that developed in these phases as a result of quenching from high sintering pressure and temperature and the mismatch of the thermo-mechanical properties of SiC matrix and diamond inclusions were evaluated. The matrix-inclusion concept has also been used to calculate stress partition in the phases of the TSDC products that can be directly comparable with the experimental data and give clearer interpretation of the experimental results. © 2021 by Trans Tech Publications Ltd.
  • No Thumbnail Available
    Item
    Wear resistance and microstructural study of diamond coated WC tools
    (Trans Tech Publications, 2010-08-02) Boland, JN; Li, XS; Rassool, RP; MacRae, CM; Wilson, NC; Elbracht, S; Luzin, V; Imperia, P; Sobott, B
    Diamond composite materials are classified as superhard and exhibit exceptional abrasive resistance. Cemented tungsten carbide tools with a thick coating of diamond composite material (PCD) are finding increased usage in materials cutting operations in manufacturing, mining, minerals, gas and petroleum exploration and civil construction industries. Two major advantages derived from these coated tools are: (a) increased wear resistance and hence increased life-span of these tools and (b) their proven ability to handle “difficult-to-machine” materials as well as high-strength, extremely abrasive materials such as quartz-rich rocks, granites and basalts. In this research, the variability of the wear resistance of PCD coated tungsten carbide is correlated with microstructural variations. A detailed study of the microstructure and distribution of phases was performed using SEM, cathodoluminescence (CL) imaging, direct x-ray imaging, Raman spectroscopy as well as residual stress measurements using neutron diffraction. © 2010 Trans Tech Publications Ltd